| 性能項目 |
試驗條件[狀態(tài)] |
測試方法 |
測試數(shù)據(jù) |
數(shù)據(jù)單位 |
| 基本性能 |
吸水率 |
24hr，in 23℃ |
ASTM D-570 |
0.20 |
% |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.20 |
--- |
| 透光率 |
厚度3mm |
ASTM D-1003 |
88 |
% |
| 折射率 |
--- |
ASTM D-542 |
1.585 |
--- |
| 阻燃性 |
厚度1.47mm |
UL 94 |
94V-2 |
--- |
| 阻燃性 |
厚度3.05mm |
UL 94 |
94V-2 |
--- |
| 機械性能 |
frame="void">
| 拉伸強度 |
屈服點 |
| 斷裂點 |
|
--- |
frame="void">
| ASTM D-638 |
| ASTM D-638 |
|
frame="void">
| 62(630) |
| 78(800) |
|
frame="void">
| Mpa(kgf/cm2) |
| Mpa(kgf/cm2) |
|
| 拉伸模量 |
--- |
ASTM D-638 |
2130(21700) |
Mpa(kgf/cm2) |
frame="void">
| 拉伸率 |
屈服點 |
| 斷裂點 |
|
--- |
frame="void">
| ASTM D-638 |
| ASTM D-638 |
|
|
--- |
| 彎曲強度 |
--- |
ASTM D-790 |
90(920) |
Mpa(kgf/cm2) |
| 彎曲模量 |
--- |
ASTM D-792 |
2260(23000) |
Mpa(kgf/cm2) |
| 壓縮強度 |
--- |
ASTM D-695 |
76(780) |
Mpa(kgf/cm2) |
| 耐沖擊強度值 |
艾氏、帶缺口厚度3.2mm |
ASTM D-256 |
830(85) |
j/m(kgf.cm/cm) |
| 耐沖擊強度值 |
艾氏、帶缺口厚度6.4mm |
ASTM D-256 |
130(13) |
j/m(kgf.cm/cm) |
| 洛氏硬度 |
--- |
ASTM D-785 |
77 |
洛氏硬度 |
| 電氣性能 |
耐導電徑跡性（CTI） |
--- |
IEC 112 |
300 |
V |
| 絕緣破壞強度 |
快速加壓值厚度1.6mm |
ASTM D-149 |
30 |
KV/mm |
| 體積電阻率 |
--- |
ASTM D-257 |
3 |
1016Ω.cm |
| 介電率 |
60Hz |
ASTM D-150 |
2.95 |
--- |
| 介電率 |
106Hz |
ASTM D-150 |
2.9 |
--- |
| 介電正切 |
60Hz |
ASTM D-150 |
0.0004 |
--- |
| 介電正切 |
106Hz |
ASTM D-150 |
0.009 |
--- |
| 耐電弧性 |
--- |
ASTM D-495 |
110 |
sec |
| 加工性能 |
frame="void">
| 成型收縮率 |
流動方向 |
| 垂直方向 |
|
--- |
frame="void">
| ASTM D-955 |
| ASTM D-955 |
|
frame="void">
| 0.5～0.7 |
| 0.5～0.7 |
|
|
| 熱 性 能 |
負荷撓曲溫度 |
負荷0.451MPa(4.6kgf/cm) |
ASTM D-648 |
142 |
°C |
| 負荷撓曲溫度 |
負荷1.813MPa(18.6kgf/cm) |
ASTM D-648 |
132 |
°C |
frame="void">
| 線膨脹系數(shù) |
流動方向 |
| 垂直方向 |
|
--- |
frame="void">
| ASTM D-696 |
| ASTM D-696 |
|
|
frame="void">
| 10-5cm/cm/℃ |
| 10-5cm/cm/℃ |
|
frame="void">
| 溫度指數(shù) |
電學式 |
| 沖擊式 |
| 非沖擊式 |
|
frame="void">
| 厚度1.47mm |
| 厚度1.47mm |
| 厚度1.47mm |
|
frame="void">
| UL 746B |
| UL 746B |
| UL 746B |
|
frame="void">
| 125 |
| 115 |
| 125 |
|
|