沙伯基礎創(chuàng)新PC LEXAN EXL9330 產(chǎn)品特性及用途：無鹵防火，5VA阻燃，耐低溫－40℃，韌性好，抗紫外線，良好的可加工性，瓷白，用于手機外殼和低溫寒冷使用產(chǎn)品

我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權威資料請致電13268582149

PC EXL9330 物性表：

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D792
Density	1.19	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	10	g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	9.00	cm³/10min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	0.40 to 0.80	%	Internal Method
Molding Shrinkage - Across Flow (3.20 mm)	0.40 to 0.80	%	Internal Method
Water Absorption (Saturation, 23°C)	0.35	%	ISO 62
Water Absorption (Equilibrium, 23°C, 50% RH)	0.15	%	ISO 62
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus 2	2100	MPa	ASTM D638
Tensile Modulus	2100	MPa	ISO 527-2/1
Tensile Strength 3 (Yield)	58.6	MPa	ASTM D638
Tensile Stress (Yield)	55.0	MPa	ISO 527-2/50
Tensile Strength 3 (Break)	61.4	MPa	ASTM D638
Tensile Stress (Break)	60.0	MPa	ISO 527-2/50
Tensile Elongation 3 (Yield)	6.0	%	ASTM D638
Tensile Strain (Yield)	6.0	%	ISO 527-2/50
Tensile Elongation 3 (Break)	130	%	ASTM D638
Tensile Strain (Break)	130	%	ISO 527-2/50
Flexural Modulus 4 (50.0 mm Span)	2070	MPa	ASTM D790
Flexural Modulus 5	2200	MPa	ISO 178
Flexural Strength 5, 6	85.0	MPa	ISO 178
Flexural Strength 4 (Yield, 50.0 mm Span)	88.9	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength 7			ISO 179/1eA
-30°C	60	kJ/m²
23°C	75	kJ/m²
Charpy Unnotched Impact Strength 7			ISO 179/1eU
-30°C	No Break
23°C	No Break
Notched Izod Impact			ASTM D256
-50°C	590	J/m
-30°C	680	J/m
23°C	800	J/m
23°C, 6.40 mm	640	J/m
Notched Izod Impact Strength
-30°C 8	55	kJ/m²	ISO 180/1A
-30°C 9	65	kJ/m²	ISO 180/4A
23°C 8	70	kJ/m²	ISO 180/1A
23°C 9	80	kJ/m²	ISO 180/4A
Unnotched Izod Impact 10 (23°C)	1100	J/m	Internal Method
Unnotched Izod Impact Strength 8			ISO 180/1U
-30°C	No Break
23°C	No Break
Instrumented Dart Impact (23°C, Total Energy)	52.9	J	ASTM D3763
Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness (H 358/30)	90.0	MPa	ISO 2039-1
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm)	134	°C	ASTM D648
Heat Deflection Temperature 11 (0.45 MPa, Unannealed, 100 mm Span)	135	°C	ISO 75-2/Be
Deflection Temperature Under Load			ASTM D648
1.8 MPa, Unannealed, 3.20 mm	121	°C
1.8 MPa, Unannealed, 6.40 mm	124	°C
Heat Deflection Temperature 11 (1.8 MPa, Unannealed, 100 mm Span)	124	°C	ISO 75-2/Ae
Vicat Softening Temperature	142	°C	ASTM D1525 12
Vicat Softening Temperature