杜邦PA6 ZYTEL 73G45L 產(chǎn)品特性：含45%玻纖增強，自潤滑，高光澤，良好的剛性，良好的強度，良好的表面光潔度，用于家電部件，體育用品，高光閃點等應(yīng)用
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
PA6 73G45L 物性表：
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
| 1.60 mm | 0.10 | -- | % | |
| 3.20 mm | 0.20 | -- | % | |
| Molding Shrinkage - Across Flow | Internal Method | |||
| 1.60 mm | 1.0 | -- | % | |
| 3.20 mm | 0.90 | -- | % | |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow: 2.00 mm | 0.90 | -- | % | |
| Flow: 2.00 mm | 0.15 | -- | % | |
| Water Absorption (Saturation, 23°C) | 4.9 | -- | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus (23°C) | 14500 | 9700 | MPa | ISO 527-2 |
| Tensile Strength (23°C) | 214 | 145 | MPa | ASTM D638 |
| Tensile Stress (Break, 23°C) | 230 | 160 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.0 | 5.0 | % | ASTM D638 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus (1 hr) | -- | 9400 | MPa | ISO 899-1 |
| Tensile Creep Modulus (1000 hr) | -- | 7300 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 12100 | 7000 | MPa | ASTM D790 |
| Flexural Modulus (23°C) | 13000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 19 | 23 | kJ/m² | |
| 23°C | 20 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 120 | 100 | kJ/m² | |
| 23°C | 120 | 110 | kJ/m² | |
| Notched Izod Impact (23°C) | 190 | 240 | J/m | ASTM D256 |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 18 | 24 | kJ/m² | |
| Unnotched Izod Impact (23°C) | 1500 | 1500 | J/m | ASTM D4812 |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 221 | -- | °C | ASTM D648 |
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 221 | -- | °C | ISO 75-2/B |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 213 | -- | °C | ASTM D648 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 213 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 221 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 0.000016 | -- | cm/cm/°C | ASTM E831 |
| CLTE - Flow (23 to 55°C) | 0.000016 | -- | cm/cm/°C | ISO 11359-2 |
| CLTE - Transverse (23 to 55°C) | 0.00010 | -- | cm/cm/°C | ASTM E831 |
| CLTE - Transverse (23 to 55°C) | 0.00010 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
| Flame Rating - UL (1.50 mm) | HB | -- | UL 94 |